Properties: White ,granule structure or dust-free particle.Please refer to the detailed instruction of each item
Product List:
| |
Item |
Basic Material |
Antimony Trioxide Masterbatch
|
|
PE Base |
|
PE Base |
|
PVC Resin Base |
|
PA Nylon 6 Base |
|
CPE Resin Base |
|
SAN Apply to ABS |
|
PS Base |
|
PP Base |
Flame retardant Masterbatch
|
|
PA Base |
|
PP Base |
|
PP Base |
|
PP Base |
|
PP Base |
|
PO Base |
Application and Character: High efficiency ,less-toxicity ,and environment (clean) character of this high consistency antimony trioxide masterbatch are being accepted by more and more customers in Europe,Canada， Japan and some other countries.It is also used as the substitute of antimony trioxide in blending industry. This product is made from high quality antimony trioxide by our unique process and disperse technique.According to their equipment features, customers can adopt granule or dust-free masterbatch.It is mainly used in granule of engineering plastics and fire retardant of plastics masterbatch production field.
Packing：25 kg/ Wpp Bag (with liner PE bag ),1 Ton /pallet ,stored in bleak & dryness area.
Compared with Antimony Trioxide Powder:
Particle Masterbatch |
Granule Masterbatch |
Antimony Trioxide Powder |
Sb2O3 is covered with plastic,toxicity reduced acutely. |
Sb2O3 is covered with plastic, toxicity reduced acutely. |
This material can lead to cancer and sensitivity. Micron powder ,need good aeration equipment inproduction. |
Dust-free particle ,not easy to pollute and without cleanout problem on equipment. |
Without cleanout problem on equipment |
Equipment easy to be polluted by powder ,thus need more time to clean.. |
Particle ,anomaly on surface and secondary material ,plastic granule not easy to be conglutination ,dispersed equalitly . |
In compounding process masterbatch is higher than plastic granule ,easy to sink and dispersed not equally. |
Micron powder and granule plastic and in transitted equipment |
Antimony Trioxide readily dispersed in the masterbatch |
Antimony Trioxide readily dispersed in the masterbatch |
Actualize fire retardant performance Antimony Trioxide need further dispersed |
Easy to actualize automaticly enter material
|
Easy to actualize automaticly enter material |
Easy to be delayed in entering material course and influnce production and quality. |
PE90 Application Example
Performance and Material
|
ABS |
HIPS |
PPH 20% Talcum Powder |
PC/ABS Alloy |
Final Product Fire Retardant Performance UL94 |
V0 1.6mm |
V0 1.6mm |
V0 1.6mm |
V0 1.6mm |
IZOD (J/m) |
200 |
85 |
40 |
500 |
VICAT (5Kg) |
95 |
84 |
95 |
110 |
ASTM D1238 |
20 - 40 |
10 - 20 |
15 - 25 |
25 - 40 |
- |
50ABS |
84HIPS |
70 PPH Melting Index 20 |
60 PC Melting Index 10 |
- |
30 SAN Melting Index 80 |
- |
5 EPDM |
25 ABS |
Decabromodiphenyl Oxide |
14-16 |
12-14 |
18-22 |
10-13 |
Antimony Trioxide Masterbatch PE90 |
5 - 6 |
4 - 6 |
7 - 9 |
4 - 5 |
PTFE |
0.2 |
0.2 |
0 |
0.2 |
Other secondary material in production |
Reply on detailed material |
PA80 Application Example :
| Performance and Material
|
PA6 |
PA6 GF30 |
PA66 |
PA66 GF30 |
Final Product Fire Retardant Performance UL94 |
V0 1.6mm |
V0 1.6mm |
V0 1.6mm |
V0 1.6mm |
|
PDBS-80 US.Great Lakes |
20 - 25 |
23 - 24 |
20 - 25 |
23 - 24 |
Antimony Trioxide Masterbatch PA80 |
10 - 12 |
9 - 10 |
10 - 12 |
9 - 10 |
|
Rely on detailed material
|
PVC85 Application Example :
Performace and Material |
Soft PVC (DOP 60 phr) |
Soft PVC (DOP 40 phr) |
Final Product Fire Retardant Performance |
27 |
31 |
|
Antimony Trioxide Masterbatch PVC 85 |
6 phr |
6 phr |
Other secondary material in production |
Rely on detailed material |
|